Original Article Forest Products Science and Tecnology

Use of Populus deltoides wood in the Production of MDP and HDP

Pâmela Caroline Lau Sozim, Everton Hillig, Raquel Marchesan, Fabiane Salles Ferro

http://dx.doi.org/10.1590/2179-8087-FLORAM-2020-0090 FLORAM, vol.28, n4, e20200090, 2021
PDF
PDF
SciELO
Downloads: 0
Views: 481

Abstract

The aimed to evaluate the properties of MDP and HDP panels, produced with pure Populus deltoides or in a mixture with Pinus taeda, together with urea-formaldehyde resin. The density and chemical properties of this wood with 8 and 12 years of age were determined, which were used for the production of panels with nominal density of 0.65 and 0.90 g.cm-3. Water absorption and thickness swelling tests were performed after 2 and 24 hours of immersion, as well as static bending and perpendicular tensile. Populus deltoides wood was classified as low-density in both ages and presented chemical properties similar to Pinus taeda. Mechanical properties obtained for the panels produced reached the minimum requirements values established by the standards NBR 14810-2 and ANSI A208.1, demonstrating the potential use of wood species for the production of MDP and HDP panels, at both ages studied and used pure or mixed with Pinus taeda wood.

Keywords

Poplar; Pinus taeda; Chemical properties; Panels; Physical-mechanical properties

References

  • American National Standards Institute. ANSI A208.1: mat-formed wood particleboard - specifications. Gaithersburg; 2009.

  • Arauco Forest Brasil SA. Resumo público do manejo florestal: regiões de Campo do Tenente e Sengés. 2018.

  • Arce JE. Modelagem da estrutura de florestas clonais de Populus deltoides Marsh. através de distribuições diamétricas probabilísticas. Ciência Florestal 2004; 14(1): 149-164.

  • Associação Brasileira de Normas Técnicas. NBR 11941: madeira - determinação da densidade básica. Rio de Janeiro; 2003.

  • Associação Brasileira de Normas Técnicas. NBR 14853: madeira - determinação do material solúvel em etanol: tolueno e em diclorometano. São Paulo; 2002.

  • Associação Brasileira de Normas Técnicas. NBR 14810-2: chapas de madeira aglomerada - parte 2 - requisitos. Rio Janeiro; 2013.

  • Benites PKRM, Lopes AS, Gouvêa AFG, Silva FC, Souza CCB. Caracterização tecnológica da madeira de híbridos de eucalipto irrigados e fertirrigados. Ciência Florestal 2018; 28 (4): 1716-1728.

  • Berneck SA. Resumo público 2019: Gilson Mueller Berneck e Florestal Segundo Planalto; 2019.

  • Bianche JJ, Carneiro ACO, Vital BR, Pereira FA, Santos RC, Soratto DN. Propriedades de painéis aglomerados fabricados com partículas de eucalipto (Eucalyptus urophylla), paricá (Schizolobium amazonicum) e vassoura (Sida spp.). Cerne 2012; 18 (4): 623-630.

  • Borodowski ED. Álamos y sauces en el Delta del Paraná: situación del sector y silvicultura. Actas Jornadas de Salicáceas 2006; 61-70.

  • Carneiro ACO, Castro AFN, Castro RVO, Santos RC, Ferreira LP, Damásio RAP et al. Potencial energético da madeira de Eucalyptus sp. em função da idade e de diferentes materiais genéticos. Árvore 2014; 38 (2): 375-381.

  • Fonte APN, Trianoski R, Iwakiri S, Anjos RAM. Propriedades físicas e químicas da madeira de cerne e alburno de Cryptomeria japonica. Revista de Ciências Agroveterinárias 2017; 16(3): 277-285.

  • Forest Stewardship Council (FSC). Public certificate search. [cited 2020 feb. 19]. Available from: Available from: https://info.fsc.org/certificate.php?lang=POR
    » https://info.fsc.org/certificate.php?lang=POR

  • Frihart CR, Hunt CG. Adhesives with wood materials: bond formation and performance. In: Forest Products Laboratory. Wood Handbook - Wood as an engineering material. Ed. Centenária. Madison: USDA; 2010.

  • Garcia EA, Guerra SPS, Eufrade Junior HJ, Sansígolo A, Lanças KP, Yamaji FM. Análise química da madeira com casca em sistemas florestais de curta rotação. Árvore 2016; 40 (1): 163-171.

  • Hafezi SM, Enayati A, Hosseini KD, Tarmian A, Mirshokraii SA. Use of amino silane coupling agent to improve physical and mechanical properties of UF-bonded wheat straw (Triticum aestivum L.) poplar wood particleboard. Journal of Forestry Research 2015.

  • Hsu QE. A process for stabilizing waferboard/OSB. In: Proceedings of the Washington State University. Particleboard Symposium 21, Washington; 1987.

  • Iwakiri S, Zeller F, Pinto JÁ, Ramirez MGL, Souza MM, Seixas R. Avaliação do potencial de utilização da madeira de Schizolobium amazonicum “Paricá” e Cecropia hololeuca “Embaúba” para produção de painéis aglomerados. Acta amazonica 2010; 40(2): 303-308.

  • Iwakiri S, Trianoski R, Chies D, Tavares EL, França MC, Lau PC et al. Use of residues of forestry exploration of Pinus taeda for particleboard manufacture. Árvore 2017; 41(3).

  • Iwakiri S, Trianoski R, Raia RZ, Keinert AC, Paula CRP, Protzek GR et al. Produção de painéis aglomerados de Hevea brasiliensis (Clone RRIM 600) em mistura com três espécies de Eucalyptus utilizadas pelas indústrias de São Paulo. Scientia Forestalis 2018; 46(117): 31-39.

  • Iwakiri S, Trianoski R, Silva AL, Stüpp AM, Cabral BM, Vieira HC. Evaluatiom of physical and mechanical properties of particleboard produced from wood of Cupressus torulosa in mixture with Pinus taeda. Floresta 2020; 50(3): 1478-1485.

  • Javarini E. Caracterização das propriedades físicas e mecânicas de Populus deltoides, plantado nas várzeas do Vale Médio do Rio Iguaçu [trabalho de conclusão de curso]. União da Vitória, Centro Universitário de União da Vitória; 2011.

  • Jin XJ, Kamdem DP. Chemical composition, crystallinity and crystallite cellulose size in Populus hybrids and aspen. Cellulose Chemical Technology 2009; 43 (7-8): 229-234.

  • Klasnja B, Kopitovic S, Orlovic S. Variability of some wood properties of eastern cottonwood (Populus deltoides Bartr.) clones. Wood Science Technology 2003; 37: 331-337.

  • Kuzovkina YA, Vietto L. An update on the cultivar registration of Populus and Salix (Salicaceae). Skvortsovia 2014; 1(2): 133-148.

  • Lau PC. Produção de painéis de colagem lateral - EGP com madeira de Populus deltoides [dissertação]. Curitiba: Setor de Ciências Agrárias, Universidade Federal do Paraná; 2017.

  • Lorenzi H, Souza HM, Torres MAV, Bacher LB. Árvores exóticas no Brasil. Nova Odessa: Instituto Plantarum; 2003.

  • Medeiros JGS, Hoppe JM. Efeito da aplicação de calcário em estacas de Populus deltoides Bartr. ex Marsh cultivadas em vaso. Ciência Florestal 2002; 12 (2), 161-167.

  • Moslemi AA. Particleboard: volume 1 - Materials. London: Southern Illinois University Press; 1974.

  • Nourbakhsh A. Mechanical and Thickness Swelling of Particleboard Composites Made from Three-Year-Old Poplar Clones. Journal of Reinforced Plastics and Composites 2010; 29(4).

  • Pereira GF, Rios PD, Buss R, Vieira HC, Grubert W, Cunha AB et al. Painéis de madeira aglomerada de Eucalyptus badjensis e Pinus spp. Scientia Forestalis 2017; 45(114): 373-382.

  • Rios PD, Pereira GF, Vieira HC, Grubert W, Cunha AB, Brand MA. Avaliação do potencial da madeira de Pinus patula Schltdl. & Cham para a produção de painéis de madeira aglomerada. Scientia Forestalis 2016; 44(110): 497-508.

  • Sanches FL, Hillig E, Iwakiri S, Napoli LM. Resistência de painéis aglomerados produzidos com mistura de madeira de espécies florestais tradicionais e não tradicionais. Ciência Florestal 2016; 26(2): 559-569.

  • Soares VC, Bianchi ML, Trugilho PF, Höfler J, Pereira AJ. Análise das propriedades da madeira e do carvão vegetal de híbridos de eucalipto em três idades. Cerne 2015; 21(2): 191-197.

  • Sozim PCL, Napoli LM, Ferro FS, Mustefaga EC, Hillig E. Propriedades de painéis aglomerados produzidos com madeiras de Ligustrum lucidum e Pinus taeda. Pesquisa Florestal Brasileira 2019; 39: 1-8.

  • Sociedade Brasileira de Silvicultura (SBS). Fatos e números do Brasil florestal. São Paulo; 2006.

  • Technical Association of the Pulp and Paper Industry. TAPPI 204cm-97: solvent extractives of wood and pulp. Atlanta; 1997.

  • Technical Association of the Pulp and Paper Industry.. TAPPI 207 cm-99: water solubility of wood and pulp. Atlanta; 1999.

  • Technical Association of the Pulp and Paper Industry. TAPPI 211 om-02: ash in wood, pulp, paper and paperboard - combustion at 525°C. Atlanta; 2002.

  • Technical Association of the Pulp and Paper Industry. TAPPI 212 om-02: one percent sodium hydroxide solubility of wood and pulp. Atlanta; 2002.

  • Technical Association of the Pulp and Paper Industry. TAPPI 222 om-02: acid-insoluble lignin in wood and pulp. Atlanta; 2002.

  • Technical Association of the Pulp and Paper Industry. TAPPI 252 om-02: pH and electrical conductivity of hot water extracts of pulp, paper, and paperboard. Atlanta; 2002.

  • Trianoski R, Iwakiri S, Matos JLM, Prata JG. Viabilidade da utilização de Acrocarpus fraxinifolius em diferentes proporções com Pinus spp. para produção de painéis aglomerados. Scientia Forestalis 2011; 39 (91): 343-350.

  • Trianoski R, Iwakiri S, Matos JLM, Chies D. Utilização da madeira de Cryptomeria japonica para produção de painéis aglomerados. Scientia Forestalis 2013; 41(97): 57-64.

  • Trianoski R, Iwakiri S, Matos, JL. Avaliação de painéis aglomerados de Toona ciliata produzidos com diferentes densidades e teores de resina. Madera y Bosques 2014; 20 (3): 49-58.

  • Trianoski R, Piccardi ABR, Iwakiri S, Matos JLM, Bonduelle GM. Incorporação de Grevillea robusta na produção de painéis aglomerados de Pinus. Floresta 2016; 46(2): 259-267.

  • Trianoski R, Iwakiri S, Machado L, Rosa TS. Feasibility of Cordia trichotoma (Vell.) wood and its by-products for particleboard manufacturing. Journal of Sustainable Forestry 2017; 1-14.

  • Vidaurre GB, Carneiro ACO, Vital BR, Santos RC, Valle MLA. Propriedades energéticas da madeira e do carvão de paricá (Schizolobium amazonicum). Árvore 2012; 36(2): 365-371.

  • VitaL BR, Haselein CR, Della Lucia RM. Efeito da geometria das partículas nas propriedades das chapas de madeira aglomerada de Eucalyptus grandis (Hill ex-Maiden). Árvore 1992; 16(1): 88-96.

Submitted date:
11/12/2020

Accepted date:
07/21/2021

617c51f2a9539535455fab53 floram Articles
2179-8087 (Electronic)
FLORAM ©2024 All rights reserved.

FLORAM

Share this page
Page Sections