The present study aimed to estimate the modulus of elasticity (MOE) at static bending of Rose gum (Eucalyptus grandis) heartwood and sapwood through two nondestructive techniques: ultrasound and stress wave. Sixty samples of heartwood and sapwood were prepared. Nondestructive tests were performed using ultrasound and stress wave timer equipment, while destructive tests were carried out in a universal machine through static bending tests. The main results showed that the heartwood presented better behavior than the sapwood in the nondestructive tests. However, the best model was obtained considering both wood types through the ultrasonic technique. Therefore, stress wave and ultrasonic techniques could be employed to estimate the modulus of elasticity of Rose gum wood.

O presente estudo objetivou estimar o módulo de elasticidade à flexão estática da madeira de cerne e alburno de Eucalyptus grandis, por meio de duas técnicas não destrutivas: ultrassom e ondas de tensão. Para tal, 60 amostras de cerne e alburno foram preparadas. Os testes não destrutivos foram realizados por meio de um equipamento de ultrassom e um de ondas de tensão, enquanto que os testes destrutivos de flexão estática foram realizados em uma máquina universal de ensaios. Os principais resultados mostraram que a madeira de cerne apresentou melhor comportamento nos ensaios não destrutivos, quando comparada à madeira de alburno. No entanto, o melhor modelo matemático foi obtido considerando-se cerne e alburno, quando estes foram analisados por meio da técnica ultrassônica. Dessa maneira, concluiu-se, no presente estudo, que as técnicas de ondas de tensão e ultrassom podem ser empregadas com o intuito de estimar o módulo de elasticidade da madeira de Eucalyptus grandis.